Refractories for Blast Furnace

Ceramic Cup Brick

  Hal-graphitised Carbon Silicon Carbide Brick  

G.V

T.V

G.V

T.V

G.V

T.V

AL₂O₃(%)

≥85

85.42

64~68

65.49

C≥30

48.1

C(%)

　

　

　

　

SiC≥50　　

51.2

C+SiC(%)

　

　

13~15

14.32

　

　

≤15

13

≤16

12.7

≤15

12.3

（g/cm³)Bulk Density

≥3.0

3.09

≥2.75

2.82

≥1.95

2.13

（Mpa) Cold Crushing Strength

≥100

181.5

≥60

83

≥40

84.3

（MPa) Cold Modulus of Rupture

≥20

20.4

　

　

≥12

25.1

（℃） Refractoriness Under Load(2kg/cm²)T_0.6  

≥1650

1700

　

　

　

　

　

　

≥100

＞100

　

　

（μm)  Average Pore Size  

　

　

≤1